Sammanfattning: About half of the restorations made on teeth today are restorations of old
fillings, which explain the need for a better dental material. Recently
Calcium aluminates as dental materials, CACs, entered the market and have
shown good potentials. However their main disadvantage is slow development
of mechanical properties. By combining CACs with Glass ionomer cements,
GICs, that obtain most of their material properties during the first couple
of hours after placement, into a hybrid, this problem could be solved.
The main reason for believing in a successful hybridization is the similar
ion release taking place during the hydration and hardening processes in
both GICs and CACs. CACs dissolve into Ca and aluminate ions when mixed
with water, an analogue to the dissolution of glass in GICs into calcium
and aluminum ions when mixed with a Polyelectrolyte, most commonly Poly
(acrylic acid), PAA. With both a cross linking of the PAA and a hydrate
precipitation that contribute to the strength development, a rapid initial
strength would be obtained that continues to improve with time. The aim of
this thesis work was to explore the possibilities of manufacturing this
hybrid, a "Biomer", to optimize candidate compositions and to evaluate the
mechanical properties of the "Biomer"-candidates.
The work was divided into two parts: a pre-study was performed in order to
find suitable constituents for the Biomer and to determine whether the CAC
and the GIC reactions were compatible, and part two was the actual
manufacturing of the Biomer. During the pre-study it was concluded that the
two systems could co-react and that the hybrid should besides CA also
contain the commercial GIC ChemFlex, manufactured by Dentsply. As reactive
agent ChemFlex liquid, major constituent PAA, and distilled water
containing Li+ (accelerator) was used. Two candidates with different GIC-CA
compositions were tested in terms of mechanical properties and the
microstructure was imaged using scanning electron microscopy (SEM).
The conclusion made from the results obtained was that hybridization ....
Detta arbete presenteras i samarbete med LIBRIS/Uppsök
...läs fortsättningen genom att logga in dig.
 |
För att komma åt denna sida måste du
vara medlem och inloggad.
|
 |
Är du inte redan medlem?
Bli medlem nu!
|
Om du loggar in får du tillgång till
Författarprofil
Har du en favoritförfattare på Mimers? Då kan du läsa allt om honom eller henne här. Du kan se bild, personlig information, statistik, listor och mycket mer!
Gästböcker
Läs vad andra har skrivit i din favoritförfattares gästbok. Du kan även starta en debatt, kommentera , rösta på de arbetet som ligger uppe samt skriva inlägg i forumet.
Se hela arbeten
Är du intresserad av något speciellt som du vet att en medlem på Mimersbrunn skrivit ett arbete om? Du får även tillgång till andras arbeten, sätta betyg samt att kommentera.
Nyckelord
Dental, Materials, Biomer, Calcium aluminates, Glass
Ionomers, Cements, Poly(acrylic acid), Hybridization,
Taggar
En tag är ett sökord eller uppmärkning av ett arbete. Genom att märka upp arbeten med olika relevanta sökord, kan du lätt hitta tillbaks till de arbeten du är intresserad av, genom att söka på dessa ord nästa gång du besöker vår sajt. Man kan också se och söka på andra besökares taggar.