AbstractToday sheet metal forming is used to make a variety of mass production because it has a high production rate. One of the biggest concerns in sheet metal forming is wear of the tool in form of galling. Galling in sheet metal forming is characterised by an increased tool surface roughness, unstable friction in the forming process and undesirable scratches on the final products.Several ways of ranking materials resistance to galling exist today but only ASM G98 is standardised. Nevertheless, some different methods developed for ranking tool materials’ tendency to galling have also been developed.The aim of this thesis is to develop and improve the Uddeholm Tooling Tribo Test rig located at Uddeholm Tooling AB. The rig, which is a variation of cylinder-on-cylinder test equipment, was improved with a new tool holder, a utilization of the real sheet material counter face and a new data acquisition system and software. The galling was detected using scratches on the sheet, metallographic analysis of the material adhered on the tool specimen, monitoring of coefficient of friction and the standard deviation of the coefficient of friction.The obtained results show difficulties with ranking of tool materials in terms of galling resistance under non-lubricated conditions. The tool steels tested were SVERKER21 and UNIMAX. AISI304-10, DC04 and DOCOL1000DP sheets were used. Additionally a low friction coating of BalinitC on SVERKER21 was also included. All specimens of the tool steels showed signs of galling on every run, only the low friction coating showed a transition in behaviour of friction coefficient corresponding to galling initiation. The standard deviation of the coefficient of friction increased at low loads. A decrease of the test loads led to stability loss of the system detected by an increase in the standard deviation of the co...